德国MPO涂层测厚仪/菲希尔MPO涂层测厚仪

DUALSCOPE MP0涂层测厚仪（磁性/非磁性双功能）

DUALSCOPE MP0涂层测厚仪是一款为快速且简便测量而设计的涂层测厚仪。mpor涂层测厚仪这一款经济型的涂层测厚仪。MP0R涂层测厚仪可以准确地和方便地在2个液晶显示器上显示镀层、涂层厚度的读数：一块大的位于前部面板，另一块位于上部面板。mpor涂层测厚仪独特的符合人类工程学设计的集成于仪器的恒压测量探头允许方便地单手操作，mpor涂层测厚仪可以进行测量数据统计评估以及在10-20 m（33-66 feet）的距离范围内将测量数据在线或离线的无线传输至计算机的内置无线电发射器。

DUALSCOPE MP0涂层测厚仪采用根据DIN EN ISO 2360，ASTM B244标准的电涡流方法和DIN EN ISO 2178，ASTM B499电磁感应方法，被用来测量非导电涂层在非铁金属基材上的厚度以及非铁金属镀层和非导电涂层在铁或钢上的厚度。mpor涂层测厚仪能自动地识别被测材料并选择适合的测试方法。

DUALSCOPE MP0涂层测厚仪适合于测量：

• 非铁金属镀层、涂层（例如：铬，铜，锌等）在铁或钢上。

• 油漆、腊克和合成涂层在铁或钢上。

• 非导电涂层在非铁金属基材上，例如：油漆、腊克和合成涂层在铝、铜、黄铜、锌和不锈钢上。

• 铝的阳极氧化层。

mpo涂层测厚仪主要技术参数：

MP0 Coating Thickness Gauge

MPO Applications & Specifications
Anodizing thickness on anodized aluminum.	Pain thickness measurement on iron.
Measurement of zinc on iron. A calibration is mandatory for extremely curved specimens to obtain correct measurements.	Integrated hard-material-coated probe with V-notch in probe base for measurements on cylindrical parts

MPO Application Examples Electroplated coatings made of zinc, chrome, copper on steel and iron. Paint, lacquer, plastic coatings on steel and iron. Paint, lacquer, plastic coatings on non-ferrous metals (aluminum, copper, brass) or on non-magnetic stainless steel. Anodized coatings on aluminum MPO Specifications

Application	NF, Iso/Fe	Iso/NF
Thickness range	0-2000 µm	0-2000 µm
Accuracy based on Fischer standards	Up to 75 µm: ± 1.5 µm 75 to 1000 µm: < 2% 1000 to 2000 µm: < 3%	Up to 50 µm: ± 1 µm 50 to 1000 µm: < 2% 1000 to 2000 µm: < 3%
Repeatability & precision based on Fischer standards	Up to 50 µm: ± 0.25 µm 50 to 2000 µm: < 0.5%	Up to 100 µm: ± 0.5 µm 100 to 2000 µm: < 0.5%
Measurement method	Magnetic induction (DIN EN ISO 2178)	Eddy current (DIN EN ISO 2360)
Operating temperature	5-60°C (41-140°F)
Data Memory	1000 measurements
Included with shipment	Instrument & manual 604-329 2 Batteries LR6., AA, 1.5 V 603-534 Calibration standard, Fe base 603-477 Calibration standard, Aluminum base 603-478 Calibration foil, 75 μm 603-479